Quote from hyrefractory on December 25, 2025, 2:58 am

1. Introduction

In modern continuous casting steelmaking, the tundish is not merely an intermediate vessel between the ladle and the mold; it is a metallurgical reactor that plays a crucial role in steel cleanliness, temperature control, and flow optimization. To achieve these objectives, a series of functional refractory products are installed in and around the tundish. These refractory items must operate under extreme conditions, including high temperature, aggressive molten steel and slag, thermal shock, erosion, and chemical corrosion.

Among the most critical tundish-related refractories are the ladle shroud, stopper rod, seating block, and associated flow-control components such as tundish nozzles and sub-entry nozzles (SENs). Each of these items performs a specific function and must be designed with appropriate material composition, structure, and performance characteristics.

This article provides a detailed technical overview of these key refractory products, focusing on their functions, materials, working conditions, failure mechanisms, and performance requirements.

---

2. Ladle Shroud

2.1 Function of the Ladle Shroud

The ladle shroud is a tubular refractory component installed between the ladle slide gate and the tundish impact zone. Its primary function is to protect the molten steel stream from reoxidation and nitrogen pickup during transfer from the ladle to the tundish.

Key functions include:

• Creating a closed pouring system

• Preventing air aspiration and secondary oxidation

• Reducing inclusion formation

• Stabilizing the steel flow into the tundish

• Minimizing temperature loss

The ladle shroud is especially critical in the production of clean steels, such as automotive grades, IF steels, and bearing steels.

2.2 Materials and Structure

Ladle shrouds are typically manufactured from high-purity alumina-based or zirconia-containing refractories. Common material systems include:

• Al₂O₃–C (alumina-carbon)

• Al₂O₃–ZrO₂–C

• ZrO₂–C (for high-end applications)

Key material requirements:

• High thermal shock resistance

• Excellent resistance to steel and slag corrosion

• Low wettability with molten steel

• High mechanical strength at elevated temperature

Carbon is often added to improve thermal shock resistance and reduce steel adhesion, while zirconia enhances corrosion resistance and dimensional stability.

2.3 Failure Mechanisms

Typical failure modes of ladle shrouds include:

• Oxidation of carbon at high temperature

• Erosion by high-velocity steel stream

• Cracking due to thermal shock

• Joint leakage caused by improper gasket sealing

Advanced ladle shrouds may incorporate anti-oxidation coatings and optimized inner bore designs to extend service life.

---

3. Stopper Rod

3.1 Role of the Stopper Rod in Tundish Flow Control

The stopper rod is a critical flow-control refractory used in tundishes equipped with stopper-controlled casting systems. By moving vertically, the stopper rod regulates the flow rate of molten steel from the tundish to the mold through the tundish nozzle.

Main functions:

• Precise control of steel flow

• Stable casting speed

• Quick response during start and end of casting

• Emergency shut-off capability

Compared with slide gate systems, stopper rods offer finer flow control and are widely used in slab and bloom casting.

3.2 Stopper Rod Construction and Materials

A typical stopper rod assembly consists of:

• Stopper head (tip) – directly contacts molten steel

• Rod body – connects the head to the actuator

• Protective coatings or sleeves

Material systems for stopper heads commonly include:

• Al₂O₃–C

• Al₂O₃–ZrO₂–C

• MgO–C (for specific steel grades)

The stopper head must exhibit:

• Excellent erosion resistance

• High thermal shock resistance

• Minimal steel adhesion

• Dimensional stability during long casting sequences

The rod body is often made from dense alumina or fiber-reinforced refractories, sometimes protected by insulating sleeves.

3.3 Wear and Failure Issues

Common problems include:

• Erosion of stopper tip leading to unstable flow

• Build-up of alumina inclusions

• Cracking due to repeated thermal cycling

• Misalignment with the seating block

Advanced stopper designs optimize tip geometry and material gradients to improve service life and flow stability.

---

4. Seating Block

4.1 Function of the Seating Block

The seating block (also known as the upper nozzle block) is installed at the bottom of the tundish and serves as the mounting interface between the tundish lining and the tundish nozzle.

Its primary functions include:

• Supporting the tundish nozzle

• Ensuring precise alignment with the stopper rod

• Providing a tight seal to prevent steel leakage

• Withstanding high mechanical and thermal stresses

Although relatively small in size, the seating block is a critical safety component.

4.2 Material Characteristics

Seating blocks are typically produced from high-density, high-strength refractory materials, such as:

• Dense alumina

• Alumina-spinel composites

• Alumina–zirconia materials

Key performance requirements:

• High compressive strength

• Excellent thermal shock resistance

• Minimal deformation at casting temperature

• Good compatibility with nozzle and tundish lining materials

The bore accuracy and surface flatness of the seating block are extremely important for leak-free operation.

4.3 Failure Risks

Potential issues include:

• Cracking caused by thermal gradients

• Steel leakage due to poor machining tolerance

• Chemical attack from aggressive slags

• Misalignment leading to uneven stopper wear

Precision manufacturing and proper installation practices are essential to avoid these problems.

---

5. Other Important Tundish Refractory Items

5.1 Tundish Nozzle

The tundish nozzle is installed below the seating block and guides molten steel into the mold or SEN. It must resist:

• Severe erosion

• Chemical attack

• Clogging by non-metallic inclusions

Common materials include Al₂O₃–C and ZrO₂–C, often with anti-clogging additives.

---

5.2 Sub-Entry Nozzle (SEN)

The SEN connects the tundish to the mold and controls steel delivery into the mold cavity. It plays a vital role in:

• Mold flow pattern control

• Slag entrainment prevention

• Surface quality improvement

Zirconia-based SENs are widely used due to their superior corrosion resistance.

---

5.3 Impact Pad

Installed in the tundish impact zone, the impact pad absorbs the kinetic energy of incoming steel from the ladle shroud, reducing lining erosion and turbulence.

Materials are usually:

• High-alumina castables

• Spinel-containing refractories

---

5.4 Dams and Weirs

These flow-control refractories optimize steel residence time and inclusion flotation. They are usually made from insulating or alumina-based materials and are often disposable.

---

6. Integration and System Performance

The performance of tundish refractories should not be evaluated individually but as a complete functional system. Proper matching of ladle shroud, stopper rod, seating block, and nozzles ensures:

• Stable casting

• Improved steel cleanliness

• Reduced breakout risk

• Lower refractory consumption

Advanced steel plants increasingly work with refractory suppliers to develop system-based solutions rather than standalone products.

---

7. Conclusion

Refractory products such as the ladle shroud, stopper rod, and seating block are indispensable components of the tundish system in continuous casting. Each item serves a distinct function, yet all must work together under extreme thermal, chemical, and mechanical conditions.

With the increasing demand for clean steel, longer casting sequences, and higher productivity, the design and material selection of tundish refractories continue to evolve. Innovations in composite materials, anti-oxidation technologies, and precision manufacturing are pushing the performance of these refractory items to new levels.

A deep understanding of these tundish refractories is essential for steelmakers seeking to improve casting stability, product quality, and overall operational efficiency.

The difference between magnesia carbon brick and aluminum magnesia carbon brick

Production and application of isostatically pressed refractory materials

New generation ladle slide gate system for performance improvement

Thermal Stress Cracking Of Ladle Slide Gate Plate

The-damage-reasons-to-ladle-sliding-plates-and-the-advantages-and-disadvantages-of-some-slide-gate-plates

The Unseen Champion Of Continuous Steel Casting-Slide Gate

5 Key Factors Behind Ladle Shroud Cracking

How To Extend The Service Life Of Slide Gate Plates In Steel Casting - Henan Yangyu Refractories Co.,Ltd

How To Choose Ladle Shroud From A China Factory

A Few Things You Should Know About The Ladle Nozzle

Wear Reason About The Slide Gate Plate

Before Enquiry Some Questions You Should Know About Ladle Shroud - Henan Yangyu Refractories Co.,Ltd

The Iso Refractory Trial Report Compared With Vesuvius

The drawing regarding kinds of slide gate plate

Slide Gate Plate Price Guide 2025: Complete Pricing Analysis and Buying Tips

Complete Guide to Submerged Entry Nozzle (SEN) in Steel Making

What Is A Ladle Shroud And Its Function - Henan Yangyu Refractories Co.,Ltd

How To Improve The Lifespan Of Slide Gate Plates

The Reason Of Sub Entry Nozzle Clogging And How To Slove It

Why The Tundish Stopper Cracks And How To Improve It

How To Avoid The Sub Entry Nozzle(SEN) Clogging

The Problem In The Application Of Monoblock Stopper Rods

https://youtu.be/EmNn8E3hRdo

https://youtu.be/AJ3Dt9R2Rh8

https://youtu.be/ctppROYzPuc

https://www.facebook.com/share/v/18N38vvVgN/

https://www.facebook.com/share/r/1ADSPxESUu/

https://www.facebook.com/share/r/1EuCe4VH5N/

https://www.facebook.com/share/r/17n9NoNgrW/

https://www.facebook.com/share/v/1Bqy4s3ePA/

https://www.facebook.com/share/v/17Sh8YFZB9/

https://www.facebook.com/share/v/1F25QtRqJP/